FeCoVNi Permenent Magnetic P6 Alloy , Cold Rolled Strip Semi Hard Magnet Alloy

China Suzhou Xunshi New Material Co., Ltd certification
China Suzhou Xunshi New Material Co., Ltd certification
Have been business relationship for 3 years, great partner for Nickel Cobalt Alloy!

—— Daniel Weree

On-time delivery. And support is good and fast.

—— Carolina Fasio

I'm Online Chat Now

FeCoVNi Permenent Magnetic P6 Alloy , Cold Rolled Strip Semi Hard Magnet Alloy

FeCoVNi Permenent Magnetic P6 Alloy , Cold Rolled Strip Semi Hard Magnet Alloy
FeCoVNi Permenent Magnetic P6 Alloy , Cold Rolled Strip Semi Hard Magnet Alloy FeCoVNi Permenent Magnetic P6 Alloy , Cold Rolled Strip Semi Hard Magnet Alloy

Large Image :  FeCoVNi Permenent Magnetic P6 Alloy , Cold Rolled Strip Semi Hard Magnet Alloy

Product Details:
Place of Origin: China
Brand Name: AIWEN
Certification: ISO 9001:2015
Model Number: P6 alloy
Payment & Shipping Terms:
Minimum Order Quantity: 20kg
Price: Negotiable
Packaging Details: Plywood case
Delivery Time: 45-60 days
Payment Terms: T/T, Western Union
Supply Ability: 300 kg per week
Detailed Product Description
Equal Grade: 2J4(China) Form Of Supply: Cold Rolled Strip, Wire, Round Bar
Type: FeCoVNi Thickness: 0.05-0.8mm
Product Name: Permanent Magnet Alloy Certification: ISO 9001:2015
High Light:

cobalt iron alloy

,

magnetic materials

P6 alloy is a cobalt base precipitation hardened alloy which combined the advantages of high hysteresis loss and low magnetizing force. It is similar to Vicalloy-2J10 in China standard.

 

Typical chemical composition P6 alloy

Ni: 6.0%

Co: 45.0%

V: 4.8%

Fe: Balance

 

Chemical composition 2J4 (%, weight)

C: 0.12 max

P: 0.025 max

S: 0.020 max

Si: 0.70 max

Mn: 0.70 max

Co: 44.0~46.0

V: 3.5~4.5

Ni: 5.3~6.7

Fe: Balance

 

Physical properties

Density: 8.2g/cm3

Curie point: 1580°F/860°C

 

Machenical properties

Hardness:  HRC 40~46(before temper)

                   HRC 58~62 (after temper)

Tensile strength, σb: 882~1370MPa(before temper)

                                  1180~1960Mpa(after temper)

 

Thickness range: 0.05~0.8mm

Other thickness also availble per request.

 

It is required to do a age hardening heat treatment after material fabricated to the desired form.

Placed in a protective atmosphere furnace and held at 550~600 degree for two to five hours.

 

 