| Density: | 8.1g/cm3 | Melting Range: | 1530-1600°C |
|---|---|---|---|
| Cuire Piont: | 860°C | Resistance Rate: | 0.71μΩ·m |
| Forms Of Supply: | Bar, Wire, Strip | Product Name: | Permanent Magnet Alloy |
| High Light: | Cold Drawn Wire Cobalt Iron Alloy,Strip Permanent Magnet Alloy,Thickness 1.0mm Permanent Magnet Alloy |
||
Strip Thickness 0.05-1.0mm Iron-Cobalt Permanent Magnetic Alloy 2J10
StripThickness 0.05-1.0mm Iron-Cobalt Permanent Magnetic Alloy 2J10
2J10 can be precipitation hardened. It has good plasticity, and could be cold processed by forging, rolling and drawing and cutting. Usually, 2J10 is applied to motor equipment, such as hysteresis motor, hysteresis brake, etc. Fe-Co-V hysteresis alloys have good plasticity before tempering. After cold rolling (or drawing) with 90% strain, excellent hysteresis properties and strong magnetic anisotropy can be obtained, i.e. longitudinal magnetic properties are better than transverse ones. Therefore, if the wire can be used as the rotor of hysteresis motor in the manufacturing process, its performance is better, and it has more development prospects.
Chemical compositions
| Elements | Weight(%) |
| C | ≤0.12 |
| P | ≤0.25 |
| S | ≤0.02 |
| Si | ≤0.70 |
| Mn | ≤0.70 |
| Co | 51.0~53.0 |
| V | 9.5~10.5 |
| Ni | ≤0.70 |
| Fe | Rem |
2J10 Magnetic performance
|
Hμ(kA/m) (Hμ/Oe) |
Bμ/T (Bμ/Gs) |
Pμ(104J/m3) | Kμ |
| 14.4~18.4(180~230) | 0.9~1.2(9000~12000) | 3.0 | 0.58 |
Applications
High efficiency hysteresis motor rotor and hysteresis brake.
Good corrosion resistance, and not rust in the atmosphere.
Density:8.1g/cm3
Available forms
Round bar,Cold drawn wire,Cold rolled strip,Forging
2J10 strip is delivered without heat treatment at cold rolled state and can be supplied specifications range as below
Strip thickness: 0.05-1.0mm
Strip Width 5-200mm
Round bar Specification range: Φ5-200mm
Wire Specification range: Φ0.1～6.0mm