Thickness 0.05mm Iron Cobalt Permanent Magnet Alloy 2J4

Place of Origin China
Brand Name XUNSHI
Certification ISO 9001:2015
Model Number 2J4
Minimum Order Quantity 20kg
Price Negotiable
Packaging Details Plywood case
Delivery Time 45-60 days
Payment Terms T/T, Western Union
Supply Ability 300 kg per week
Product Details
Equal Grade P6(USA) Form Of Supply Cold Rolled Strip, Wire, Round Bar
Type FeCoVNi Thickness 0.05-0.8mm
Product Name Permanent Magnet Alloy Certification ISO 9001:2015
High Light

Permanent Magnetic Alloy 2J4


Thickness 0.05mm Permanent Magnet Alloy


Iron Cobalt Alloy 2J4

Leave a Message
Product Description

Iron-Cobalt Permenent Magnetic Alloy 2J4


2J4 belongs to Iron-Cobalt Permenent Magnetic Alloy,this alloy is suitable for making high efficiency hysteresis motor rotor with high operating temperature, and this alloy does not cause reduced magnetic performance in the range of + 150~ -140 ℃


In all kinds of the Magnetic Alloys, 2j4 is the one with a long time application and a large dosage.


After the years of exploration and practice, the technology and production process of the Magnetic Alloy 2J4,2J9,2J10 series products have been more improved, We have deep research and rich experience in alloy 2J4, 2J9, 2J10 products ,so we can provide high-quality products and precise technical support.


It is similar to Vicalloy-2J10 in China standard.

Chemical composition 2J4 (%, weight)

elements C P S Si Mn Co V Ni Fe
% 0.12 max 0.025 max 0.020 max 0.70 max 0.70 max 44.0~46.0 3.5~4.5 5.3~6.7 Balance


Physical properties

Density: 8.2g/cm3

Curie point: 1580°F/860°C


Machenical properties

Hardness: HRC 40~46(before temper)

HRC 58~62 (after temper)

Tensile strength, σb: 882~1370MPa(before temper)

1180~1960Mpa(after temper)



Magnetic motor rotor, Magnetic brake


Thickness range: 0.05~0.8mm

Other thickness also availble per request.


It is required to do a age hardening heat treatment after material fabricated to the desired form.

Placed in a protective atmosphere furnace and held at 550~600 degree for two to five hours.