FeCoV Permanent Magnet Alloy Cold Rolld Strip With Min Thickness 0.05mm 2J10

China Suzhou Xunshi New Material Co., Ltd certification
China Suzhou Xunshi New Material Co., Ltd certification
Have been business relationship for 3 years, great partner for Nickel Cobalt Alloy!

—— Daniel Weree

On-time delivery. And support is good and fast.

—— Carolina Fasio

I'm Online Chat Now

FeCoV Permanent Magnet Alloy Cold Rolld Strip With Min Thickness 0.05mm 2J10

FeCoV Permanent Magnet Alloy Cold Rolld Strip With Min Thickness 0.05mm 2J10
FeCoV Permanent Magnet Alloy Cold Rolld Strip With Min Thickness 0.05mm 2J10 FeCoV Permanent Magnet Alloy Cold Rolld Strip With Min Thickness 0.05mm 2J10

Large Image :  FeCoV Permanent Magnet Alloy Cold Rolld Strip With Min Thickness 0.05mm 2J10

Product Details:

Place of Origin: China
Brand Name: AIWEN
Certification: ISO9001
Model Number: 2J10

Payment & Shipping Terms:

Minimum Order Quantity: 20kg
Price: Negotiable
Packaging Details: Plywood case
Delivery Time: 45-50 days
Payment Terms: T/T
Supply Ability: 500kg per week
Detailed Product Description
Density: 8.1g/cm3 Melting Range: 1530-1600°C
Cuire Piont: 860°C Resistance Rate: 0.71μΩ·m
Forms Of Supply: Bar, Wire, Strip Thickness Range: 0.05~2.0mm
Width: 20~200mm Product Name: Permanent Magnet Alloy
High Light:

cobalt iron alloy

,

magnetic materials

2J10 FeCoV Permanent Magnet Alloy Cold Rolld Strip min. thickness 0.05mm

 

 

2J10 is an equal grade of Vicalloy I of Carpenter Tech.

 

2J10 can be precipitation hardened. It has good ductility, and could be cold processed by forging, rolling and drawing and cutting. Usually, 2J10 is applied to motor equipment, such as hysteresis motor, hysteresis brake, etc. Fe-Co-V hysteresis alloys have good ductility before tempering. After cold rolling (or drawing) with 90% strain, excellent hysteresis properties and strong magnetic anisotropy can be obtained, i.e. longitudinal magnetic properties are better than transverse ones. Therefore, if the wire can be used as the rotor of hysteresis motor in the manufacturing process, its performance is better, and it has more development prospects.

 

The corrosion resistance of 2J10 is good and it does not rust in the atmosphere.

 

Chemical composition

 

Element C P S Si Mn Co V Ni Fe
Weight(%) 0.12 max 0.025 max 0.020 max 0.70 max 0.70 max 51.0~53.0 9.5~10.5 0.70 max Rem

 

Application

2J10 is used to produce high efficiency hysteresis motor rotor and hysteresis brake. 2J10 wire can be used to make weigand wire in weigand sensor.

 

Forms of supply

Strip: thickness ≥0.05mm

Round bar diameter  ≥10mm

Wire: diameter  ≥0.20mm