UNS S31673 Special Stainless Steel 00Cr13Ni14Mo3 For Surgical Implants

Place of Origin China
Brand Name XUNSHI
Model Number 00Cr13Ni14Mo3
Minimum Order Quantity 200kg
Price Negotiable
Packaging Details Wooden case, wooden crate
Delivery Time 30-45 days
Payment Terms T/T
Supply Ability 20 ton per week

Contact me for free samples and coupons.

WhatsApp:0086 18588475571

Wechat: 0086 18588475571

Skype: sales10@aixton.com

If you have any concern, we provide 24-hour online help.

x
Product Details
Equal Grades UNS S31673, 316LVM, DIN 1.4441 Application Surgical Implants
Forms Of Supply Wire, Bar,tube,strip,pipe Specification ASTM F 138, ISO 5832-1
Product Name Special Stainless Steel
High Light

00Cr13Ni14Mo3 Special Stainless Steel

,

Surgical Implants Special Stainless Steel

,

UNS S31673 Special Stainless Steel

Leave a Message
Product Description

 

Special Stainless Steel 00Cr13Ni14Mo3 Wire Strip Bar For Surgical Implants

 

 

Su Zhou XUNSHI New Material Co Ltd can provide cost-effective surgical implants 00Cr13Ni14Mo3 for domestic and foreign customers, that can be produced in accordance with the national standard 4234.1-2017,American standard ASTM F138 or ISO5832-1 and other relevant specifications.

 

00Cr13Ni14Mo3 goes through a process of electric arc melting, followed by vacuum arc remelting that results in a highly uniform chemistry that contains a minimal amount of impurities. Due to its lack of contaminants and high resistance to corrosion, 00Cr13Ni14Mo3 is commonly used in temporary and permanent medical implants (sutures, surgical staples and bone pins) and body piercing jewelry.

 

Comparison Between Implant Quality and Commercial Quality Stainless Steel(wt%)

  Implant Quality Commercial Quality
Element ASTM F 138 ISO 5832-1 ASTM A 276
C 0.030 0.030 0.030
Mn 2.00 2.0 2.00
P 0.025 0.025 0.045
S 0.010 0.010 0.030
Si 0.75 1.0 1.00
Cr 17.00-19.00B 17.0-19.0B 16.00-18.00
Ni 13.00-15.00 13.0-15.0 10.00-14.00
Mo 2.25-3.00B 2.25-3.5B 2.00-3.00
N 0.10 0.10 0.10
Cu 0.50 0.50
Fe Balance Balance (Balance)

 

Tensile Properties of Implant Quality ASTM F 138 Bar and Wire and ISO 5832-1 Bar

  Diameter or Thickness Ultimate Tensile Strength Minimum 0.2% Yield Strength Minimum Elongation in 4D or 4WA
Standard Condition (mm) (MPa) (MPa) (%)
ASTM F 138 Annealed ≥ 1.60 min 490 190 40
ISO 5832-1 Annealed All 490– 690 190 40
ASTM F 138 Cold Worked 1.60– 38.1 min 860 690 12
ISO 5832-1 Cold Worked ≤ 22 860–1100 690 12
ASTM F 138 Extra Hard 1.60– 6.35 min 1350
ISO 5832-1 Extra Hard ≤ 8 min 1400

 

Characters:

High strength

High fatigue strength

Excellent microcleanliness

Excellent structural homogeneity

High surface finish

Good consistency

 

Applications

  • Fracture Fixation Devices
  • Bone Plates
  • Screws
  • Intramedullary Nails
  • Surgical Implant Devices
  • Surgical Instruments
  • Body piercing jewelry

Equal grades:

UNS S31673, 316LVM, DIN 1.4441

 

Forms available

  • Wire
  • Bar
  • Tube
  • Pipe
  • Strip

Cold pulled bar: specification:Φ1.0~25mm, size tolerance:± 0.01~±0.1mm;

Hot-rolled bar: specification:Φ14~75mm, size tolerance::±0.15~±0.30mm;

Wire: specification: 0.4~1.2mm, size tolerance: ± 0.01~±0.02mm;

Pipe: The specifications shall be determined through negotiation

UNS S31673 Special Stainless Steel 00Cr13Ni14Mo3 For Surgical Implants 0UNS S31673 Special Stainless Steel 00Cr13Ni14Mo3 For Surgical Implants 1UNS S31673 Special Stainless Steel 00Cr13Ni14Mo3 For Surgical Implants 2UNS S31673 Special Stainless Steel 00Cr13Ni14Mo3 For Surgical Implants 3